Abstract
AbstractThe rate and temperature dependent fracture behavior of glass‐filled polystyrene has been investigated over the crack speed range of 1013 to 1 mm/sec and in the temperature range 283 to 396°K for three environmental conditions: (i) air; (ii) water; and (iii) hot water exposure at 363°K and subsequent drying. Relationships between fracture toughness (Kc), crack speed and temperature have been obtained experimentally and analysed according to the concepts of fracture mechanics and reaction rate theories. Crack propagation in air is shown to be controlled by a β‐relaxation process associated with crazing. Activation energies of 200 ∼ 210 kj/mole in air and 80 ∼ 120 kj/mole in water are reported. At a given temperature and crack speed, the glass‐filled polystyrene is shown to display smaller crack propagation resistances in a water environment when compared with the air results. Specimens subjected to hot water exposure and then tested after drying also possess less cracking resistance. This toughness degradation phenomenon is a result of the damaging effects of the water which penetrates into the glass‐filled composite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.