Abstract
Microstructure and magnetic properties of Co/Pt multilayers with perpendicular anisotropy were studied as a function of growth temperature (TG) and ion irradiation. With increased TG, larger columnar grain size and an improved 〈111〉 texture were observed. Up to a critical temperature (Tcrit), a monotonic increase in coercivity (HC) with TG was measured, followed by a decrease in HC with further increase in TG. Magnetic domains of films grown below Tcrit were irregular, with their submicron size decreasing gradually with increasing TG. Films grown at 390 °C>Tcrit had fine domains on the sub-100 nm length scale. Both HC and domain size were reduced after the multilayers were exposed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.