Abstract
AbstractRecently it was proposed, that the hampered formation of external protective chromia scales on FeCr‐alloys in water vapour containing, low‐pO2 gases is correlated with enhanced internal oxidation of chromium. In the present study the internal oxidation kinetics of Fe10Cr (in mass%) during isothermal oxidation in ArH2H2O mixtures at temperatures in the range 800–1050 °C has been investigated. It was found that the tendency for Cr to become internally oxidized decreased with decreasing temperature. At the higher test temperatures the internal oxide precipitates consisted of Fe/Cr‐spinel. With decreasing temperature the precipitates near the oxidation front gradually exhibited increasing amounts of chromia. At 900 °C the oxidation morphology in the ArH2 base gas mixture changed from exclusive internal oxidation of Cr at a water vapour content of 2% towards a combined internal Cr oxidation and external Fe‐oxide formation at higher water vapour partial pressures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.