Abstract

Results of a transmission electron microscopy study of the defect structure in iron neutron-irradiated to low fluences (less than or equal to 1 dpa) at temperatures of 455 to 1013/sup 0/K are presented. The dislocation microstructures coarsen with increasing irradiation temperature from decorated dislocations, through clusters of dislocation loops, to near-edge, interstitial dislocation loops with b = a<100>, and network segments. Significant cavity formation occurred only at 548 to 723/sup 0/K, with homogeneous distributions found only at 623 and 673/sup 0/K. The maximum swelling of 0.07% occurred at 673/sup 0/K. Large cavities had a truncated octahedral shape with (111) facets and (100) truncations. Damage halos were observed around boron-containing precipitates. The effects of interstitial impurities on microstructural development and the differences in the observed microstructures compared to those in refractory bcc metals are discussed. 8 figures, 6 tables.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.