Abstract
TEM study of junctions between martensite packets (laths) and their microstructure in low-carbon martensitic steel were studied. It was revealed that formation of slip bands commences at junctions between laths. Heavy changes in microstructure occur at junctions of packets and in the near-boundary laths because of plastic deformation of martensite. A number of typical junctions between the laths after LCF are considered. Deformation process within the individual packet occurs inhomogeneously, some of the laths deform more heavily than the others. The coarser slip bands group within large laths and run along their whole lengths. It was shown that the above microstructure changes strongly affect the cyclic fracture of the steel. Some concrete sites of microcrack initiation are indicated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.