Abstract
Nickel-base alloys are widely used in nuclear Pressurized Water Reactors (PWRs). Most of them have been found susceptible to Stress Corrosion Cracking (SCC) in nominal PWR primary water. The time to initiation depends on the material and is longer for weld metals than for Alloy 600. This study will focus on Alloy 82, which is used in Dissimilar Metal Welds (DMWs). In service, DMWs are either in the as-welded state or have undergone a stress relief treatment. Previous SCC studies showed that the heat treatment reduces significantly the SCC susceptibility of the weld. In this context, this study focuses on the microstructure characterization of the weld in the as-welded state and in the heat-treated state. As chromium content is also a key factor for the SCC susceptibility, welds with low chromium content and medium chromium content were studied. The lower SCC susceptibility of the heat-treated welds was attributed to intergranular Cr23C6 resulting from a combined effect of heat treatment and chromium and carbon contents. These intergranular carbides could explain the better behavior of Alloy 82, compared to other nickel-base alloys.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.