Abstract
Nanostructured MgAl2O4 spinel was synthesized by a direct conversion process from cubic γ‐Al2O3. The effect of post‐annealing temperature (300°, 500°, and 800°C) on MgAl2O4 phase formation was investigated using transmission electron microscopy, selected area electron diffraction (SAED), electron energy loss spectroscopy (EELS), and energy‐dispersive spectroscopy (EDS). Relative diffraction intensities as well as lattice parameter measurements from SAED revealed that MgAl2O4 spinel structure starts forming at temperatures as low as 300°C. EELS and EDS spectrum images also revealed an increase in elemental homogeneity with increasing annealing temperature. The degree of ordering of Mg and Al between octahedral and tetrahedral sites has been determined from relative diffraction intensities. Results show that annealing to 800°C leads to a spinel phase with an order parameter of 0.78.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.