Abstract
The Y-type hexaferrite precursors was synthesized by co-precipitation, and the pivotal technological conditions, including pH value, temperature (T), rotate speed (R) and the flow velocity of salt solution (V) were discussed. The particles of precursors were studied by Laser particle size analyzer (LPS). The precursor calcined at 900°C was characterized via X-ray Diffraction (XRD), the vibrating sample magnetometer (VSM) and HP4291A impedance analyzer were used to investigated magnetic properties. The results showed that the particle sizes were around 3µm (D50) and the distribution range was from 2.28μm to 4.47μm, in the optimized technological conditions: pH = 10.50, T = 50°C, R = 300 rpm, V = 0.35 ml/min, SDBS = 0.3 g/L, the specific saturation magnetization, coercive force, residual magnetization, initial permeability and factor of quality of the sample were σs≈ 29.72A·m2·kg-1, Hc≈ 4.11/kA·m-1, σr≈ 7.74 A·m2·kg-1, μi≈ 9 and Q ≈ 18 respectively.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call