Tailoring the properties of electrospun PHBV mats: Co-solution blending and selective removal of PEO

Abstract

Microstructure, surface topography, thermal and mechanical features of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) electrospun non-woven mats were modified, modulated and tailored through blending with different polyethylene oxide (PEO) amounts (20, 30 and 50% wt/wt). The optimal parameters of the soaking protocol for the selective removal of the sacrificial polymer were accurately identified by means of scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), Fourier transform infrared attenuated total reflectance (FTIR-ATR) spectroscopy, simultaneous thermogravimetric and differential analyses (TG-DTA) and differential scanning calorimetry (DSC). The complete PEO removal after soaking in H2O for 7days with daily refreshment was confirmed. The resulting samples were only comprised of PHBV fibers characterized by a remarkable decrease of the average size with respect to the respective blends. Their surface topography was corrugated and rough and presented nodules, pits, nanopores, shallow and elongated nanostructured indents/grooves along the fiber axis. A remarkable reduction (>75%) of the tensile modulus (E) of electrospun PHBV mats (15–20MPa) was obtained, maintaining comparable elongation at break (εmax) values (20–30%).