Abstract
We performed SEM, electric field-current density measurements, capacitance-voltage testing, and X-ray diffraction analysis to study the effects of indium doping on the microstructure and electrical properties of ZnO varistors co-doped with Ga2O3 and Y2O3. Our results showed that the residual voltage ratio of the sintered samples decreased with the introduction of indium at defined aluminum and yttrium content. The introduction of indium clearly improved the nonlinear coefficient. The ZnO varistor samples showed optimal performance at a composition of 0.025mol% indium, 0.4mol% gallium, and 0.9mol% yttrium. This sample exhibited a residual voltage ratio of 1.45, a nonlinear coefficient of 76.2, a 1-mA residual voltage of 454V/mm, and a leakage current of 1.44µA/cm2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.