Abstract
Temperature-dependent characteristics of GeSn light-emitting diodes with Sn composition up to 9.2% have been systematically studied. Such diodes were based on Ge/GeSn/Ge double heterostructures (DHS) that were grown directly on a Si substrate via a chemical vapor deposition system. Both photoluminescence and electroluminescence spectra have been characterized at temperatures from 300 to 77 K. Based on our theoretical calculation, all GeSn alloys in this study are indirect bandgap materials. However, due to the small energy separation between direct and indirect bandgap, and the fact that radiative recombination rate greater than non-radiative, the emissions are mainly from the direct Γ-valley to valence band transitions. The electroluminescence emissions under current injection levels from 102 to 357 A/cm2 were investigated at 300 K. The monotonic increase of the integrated electroluminescence intensity was observed for each sample. Moreover, the electronic band structures of the DHS were discussed. Despite the indirect GeSn bandgap owing to the compressive strain, type-I band alignment was achieved with the barrier heights ranging from 11 to 47 meV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have