Abstract
Silicon carbide (SiC) detectors have great potential in nuclear fusion diagnosis and intense irradiation field measurement due to their outstanding irradiation resistance, high charge collection efficiency (CCE), and fast pulse response time. However, the irradiation resistance and the performance degradation of SiC detectors as a result of He ion irradiation remains unclear. In this article, SiC detectors based on 4H-type material with the p-i-n junction structure were prepared, and their I-V characteristics, α-particle spectra, and linearity of energy response were evaluated before and after He ion irradiation at fluences ranging from 1×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12</sup> to 3 ×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">15</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> . The preirradiated SiC detector exhibited low dark current (<; 1 nA), high CCE (98.5%), and good energy resolution (0.87%). At an He ion irradiation fluence of 1 ×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> , detector performance degradation was negligible, with no increase of dark current, CCE decreased to 85%, and a 2.2% degradation of energy resolution. At a fluence of 3 ×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">15</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> , CCE decreased to 19.3%, with an 8.57% degradation in energy resolution, but the dark current was still lower than 2 nA, with good spectra measurement capabilities and high linearity of energy response. These results indicate that the He ion irradiation resistance of 4H-SiC detectors is 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sup> times greater than silicon (Si) detectors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.