Abstract
Ternary stannides CePd3Sn and LaPd3Sn were synthesized by arc melting the elements. Their crystal structures determined at room temperature revealed a new structure type: sp. gr. Cmcm, Z = 4, a = 4.5160(18) Å, b = 15.878(8) Å, c = 5.396(3) Å for CePd3Sn and a = 4.5187(10) Å, b = 15.961(5) Å, c = 5.451(2) Å for LaPd3Sn. The new type of structure can be presented as built of two types of slabs stacked along the b-axis – CePdSn slab of PbFCl-type and palladium corrugated slab. CePd3Sn and LaPd3Sn undergo reversible crystal structure phase transition at 141 K and 260 K, respectively. The temperature hysteretic behavior through the transition is tracked with electrical resistivity and magnetic susceptibility. Single-crystal X-ray diffraction data at 120 K showed that the low-temperature (LT) polymorph of CePd3Sn crystallizes in the monoclinic structure type, with C2/m space group, Z = 16 and lattice parameters a = 10.8314(7) Å, b = 9.0474(5) Å, c = 15.8725(12) Å, β = 91.325(6)°. LT−CePd3Sn is found to order at low temperature into a putative antiferromagnetic spin structure below 1 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.