Abstract Bulk copper, copper-graphene and copper-graphite composites were produced from copper-thermally expanded graphite (TEG) powder mixtures with 0-3 wt.% TEG contents via modified powder metallurgy process that includes powder milling in a planetary mill at 350 rpm for 5 hours, compaction, and vacuum annealing at 1030 °C for 1 hour. Phase composition and microstructure of the composites were analysed by XRD and SEM techniques. According to Raman spectroscopy, TEG transforms into a few layer graphene flakes in case of composites with 0.1-1 wt.% of carbon additive, while for 3 wt.% of carbon additive it remains in the form of graphite. The addition of 0.1 wt.% TEG results in the tensile strength increase up to 160 MPa (from 93 MPa for pure copper specimen synthesized via the similar synthesis route). Vickers hardness obtained for Specimens under the study is independent fromthe composite composition.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.