Abstract
Abstract Zn x Mg 1 − x Fe 2 O 4 nanoparticles ( 0 ≤ x ≤ 1 in steps of 0.1) have been produced by centrifugation using the low temperature glycol-thermal method at 200 °C. Single-phase formation was confirmed by X-ray powder diffraction which revealed a well-defined cubic spinel structure with space group Fd3m. HRTEM and TEM were also used for the morphology studies. The crystallite size of the compounds ranged from 10.6 to 22.2 nm. A strong correlation was found between X-ray density and Zn-concentration, x . The magnetic properties as a function x were investigated by using 57 Fe Mossbauer spectroscopy, magnetization measurements using a Lakeshore vibrating sample magnetometer (VSM) at room temperature. We also report VSM measurement on a cryogen free measurement system at isothermal temperatures between 4 K and 300 K in external applied magnetic fields of up to 5 T. For x 0.8 , the room-temperature Mossbauer results show that the samples were transformed from paramagnetic state to magnetic ordered state. The temperature-dependences of saturation magnetization and coercive field follow the modified Bloch's law and Kneller's law, respectively. Strong correlation between saturation magnetization M S ( 0 ) and crystallite size D is observed. Two distinct composition ranges with Zn content are identified for which M S ( 0 ) variation with x is explained by the Neel and Yafet–Kittel models.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.