Single crystals of solid solutions Rb1−xTi1−xNbxOPO4(RTP: Nb) were grown and the temperature dependences of their dielectric and nonlinear optical properties and electric conductivity were studied. The maximum possible niobium content in these crystals is close to x = 0.1. The niobium impurities decelerate growth of {100} faces, and crystals take a plate-like habit. With increasing doping level, ferroelectric phase transitions diffuse and their temperature decreases. A specific feature of the dielectric properties of RTP: Nb crystals is the appearance of a broad relaxation maximum e33 in the temperature range 200–600°C caused by the formation of vacancies in the rubidium cation sublattice. The intensity of second-harmonic generation under laser irradiation decreases with increasing niobium content. The atomic structure of a crystal with x = 0.01 is studied and it is established that niobium substitutes for titanium only in Ti(1) positions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Crystallography Reports
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.