Abstract
A corundum-type structure of cobalt niobate (Co4Nb2O9) has been synthesized by a solid-state reaction. The formation of the Co4Nb2O9 phase in the calcined powders was investigated as a function of calcination conditions by differential thermal analysis (DTA) and X-ray diffraction (XRD) techniques. Morphology and particle size have been determined by scanning electron microscopy (SEM). It was found that the minor phases of unreacted Co3O4 tend to form together with the columbite CoNb2O6 phase at a low calcination temperature and short dwell time. It seems that the single-phase of Co4Nb2O9 in a corundum phase can be obtained successfully at the calcination conditions of 900°C for 60 min, with heating/cooling rates of 20°C /min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.