Abstract
A novel method for the synthesis of titanium hydride powder from titanium tetrachloride via the magnesiothermic reduction in an hydrogen gas atmosphere was investigated. To examine the influence of temperature on the formation of titanium hydride, the reduction was conducted at 1023~1123 K under 1 atm of hydrogen gas atmosphere for approximately 30 min. Subsequently, the titanium hydride powder was sintered by maintaining the temperature for 0~120 min, and the decrease in the oxygen concentration of the powder was investigated. The experimental results showed that TiH1.924 was produced at 1023 K, whereas mixtures of TiH1.924 and TiH1.5 were produced at 1073 K and 1123 K. In addition, the hydrogen concentration in the powder decreased with increasing temperature. The concentration of oxygen in the powder decreased with increasing temperature and sintering time owing to the decrease in the specific surface area of the powder. The minimum concentration of oxygen was 0.246 mass% when the mixture of TiH1.924 and TiH1.5 was obtained at 1073 K and a sintering time of 120 min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.