Abstract
Mordenite membrane was prepared on α-Al 2O 3 tube by in situ hydrothermal synthesis with tetraethylammonium bromide (TEABr) as template agent. By the application of aging process of the parent solution, the size of mordenite crystals could be remarkably reduced from 20–30 (without aging) to 4–5 μm. The small crystal mordenite membrane had higher performance of pure gas permeation than big crystal mordenite membrane. The ideal selectivity of H 2/N 2 was 9.80, much higher than 3.82 of big crystals mordenite membrane. The membrane displayed high water-permselective performance in pervaporation (PV) test toward water/organic liquid mixtures. The highest separation factors achieved toward water/methanol, water/ethanol, water/ n-propanol and water/ i-propanol were 2600 ( X W=50%, T=323 K), 5500 ( X W=50%, T=343 K), 6000 ( X W=15%, T=343 K) and 6800 ( X W=50%, T=343 K), respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.