Abstract
A phthalonitrile monomer (DPTP) containing pyridine with sulfide bonds was prepared and cured into polymers using different curing agents under the same temperature-programmed process. We characterized and comprehensively evaluated the effects of different curing agents on the thermal and thermomechanical properties of phthalonitrile resin, showing that the DPTP monomer cured with naphthalene-containing curing agent exhibited the best performance among the three polymers. Differential scanning calorimetric (DSC) investigation manifested that the melting point of the DPTP monomer was 61 °C, with a processing window of about 170 °C, suggesting the presence of a wide processing range. Thermogravimetric analysis (TGA) demonstrated the outstanding heat resistance, T5%, of 460 °C in nitrogen, at the same time demonstrating superior long-term stability compared with other commonly used polymer materials, which proves the long-term usage under high temperatures of 300 °C. Dynamic mechanical analysis (DMA) revealed that the storage modulus at 50 °C was 3315 MPa, and the glass transition temperature (Tg) of the polymer was more than 350 °C. Therefore, DPTP resins have favorable thermal stability as well as prominent thermomechanical properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.