Synthesis of poly(aryl ether ketone)s containing diphenyl moieties by electrophilic Friedel–Crafts solution polycondensation

Abstract

AbstractA new monomer, 4,4′‐bis(4‐phenoxybenzoyl)diphenyl (BPOBDP), was prepared by Friedel–Crafts reaction of 4‐bromobenzoyl chloride and diphenyl, followed by condensation with potassium phenoxide. Novel poly(ether ketone ketone) (PEKK)/poly(ether ketone diphenyl ketone ether ketone ketone) (PEKDKEKK) copolymers were synthesized by electrophilic Friedel–Crafts solution copolycondensation of isophthaloyl chloride (IPC) with a mixture of diphenyl ether (DPE) and BPOBDP, in the presence of anhydrous aluminum chloride and N‐methyl‐pyrrolidone (NMP) in 1,2‐dichloroethane (DCE). The copolymers obtained were characterized by various analytical techniques such as FT‐IR, DSC, TGA, and wide‐angle X‐ray diffraction (WAXD). The results showed that the resulting copolymers exhibited excellent thermal stability due to the existence of diphenyl moieties in the main chain. The glass transition temperatures are above 152°C, the melting temperatures are above 276°C, and the temperatures at a 5% weight loss are above 548°C in nitrogen. The copolymers with 50–70 mol% BPOBDP had tensile strengths of 101.5–102.7 MPa, Young's moduli of 3.23–3.41 GPa, and elongations at break of 12–17%. All these copolymers were semicrystalline and insoluble in organic solvents. Copyright © 2008 John Wiley & Sons, Ltd.