Synthesis of pH-sensitive poly(β-amino ester)-coated mesoporous silica nanoparticles for the controlled release of drugs

Abstract

This report describes the synthesis of a controlled drug delivery system that was obtained by coating mesoporous silica nanoparticles (MSNs) with poly(β-amino ester) (PbAE), which is a solid and stable material at physiological pH, but is dissolved at acidic pH values, such as those in tumor tissues (from 5.0 to 6.5). To synthesize the system, PbAE chains were grafted onto amino-functionalized MSNs through a reaction between the surface amino groups of MSNs and the ends of acrylate chains of a PbAE. The system was physicochemically characterized by dynamic light scattering (DLS), Fourier transform infrared spectroscopy, transmission electron microscopy, thermogravimetric analysis, X-ray photoelectron spectrometry, and X-ray diffraction analyses. In addition, the in vitro release of doxorubicin (DOX) and doxycycline (DXY) in acidic and physiological media was evaluated. It was observed that the PbAE modification did not affect the mesoporous structure of MSNs. When the amount of 3-aminopropyltriethoxysilane was increased during functionalization, the amount of PbAE binding to MSNs increased as well. With respect to drug release, the sample with the highest amount of PbAE showed better control in the delivery of DXY and DOX in acidic media, because at pH 5.5, the release of both drugs was 40% higher than that at pH 7.4. These results reveal two aspects about the presence of PbAE in MSNs: PbAE does not affect the mesoporous structure of the nanoparticles, and PbAE is the main factor controlling the delivery of drugs in acidic media.