Abstract

A novel sulfonated polybenzimidazole, sulfonated poly[2,2′-(p-oxydiphenylene)-5,5′-bibenzimidazole] (SOPBI), was successfully prepared by post-sulfonation reaction of the parent polymer, poly[2,2′-(p-oxydiphenylene)-5,5′-bibenzimidazole] (OPBI), using concentrated and fuming sulfuric acid as the sulfonating reagent at 80°C, and the degree of sulfonation (DS) could be regulated by controlling the reaction conditions. No significant polymer degradation was observed in the post-sulfonation processes. Direct polymerization of 4,4′-dicarboxydiphenyl ether-2,2′-disulfonic acid disodium salt (DCDPEDS) and 3,3′-diaminobenzidine (DABz), however, resulted in insoluble gels either in polyphosphoric acid (PPA) or in phosphorus pentoxide/methanesulfonic acid (PPMA) in a ratio of 1:10 by weight reaction medium. The SOPBIs prepared by the post-sulfonation method showed good solubility in dimethyl sulfoxide (DMSO), high thermal stability, good film forming ability and excellent mechanical properties. Cross-linked SOPBI membranes were successfully prepared by thermal treatment of phosphoric acid-doped SOPBI membranes at 180°C in vacuo for 20h and the resulting cross-linked membranes showed much improved water stability and radical oxidative stability in comparison with the corresponding uncross-linked ones, while the proton conductivity did not change largely. Highly proton conductive (150mScm−1, 120°C in water) and water stable SOPBI membrane was developed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.