Abstract
Sodium tantalum oxide doping lanthanum (La-NaTaO3) compounds were successfully synthesized by a sol-gel method and calcined at different temperatures. Tantalum chloride (TaCl5) was used as starting material and lanthanum nitrate (La(NO3)3.6H2O) as lanthanum source. X-ray diffraction (XRD) revealed that the calcination temperature strongly influenced the crystallinity of the prepared samples.The crystallite sizes of the resultant La-NaTaO3were in the range of 27-46 nm. The photocatalytic activities of the samples were examined for hydrogen production from an aqueous methanol solution under UV light irradiation. It was found that the photocatalytic activity of the La-NaTaO3 depended strongly on the calcination temperature. The range of calcination temperatures were 500, 700, and 900°C. The La-NaTaO3 sample calcined at 900°C showed the highest photocatalytic activity compared to the samplescalcined at the other temperatures. The rate of hydrogen production reached a value of 6.16 mmol h-1 g-1 catalyst.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.