Abstract
A new polycrystalline material Na3Co7(PO4)6 has been synthesized by solid-state (ST) and sol-gel (SG) methods and characterized using powder X-ray diffraction (XRD) to solve the structure, which is found to crystallize in the monoclinic system with a P21/c space group. Scanning electron micrographs showed the particles as aggregates with grain sizes ranging from 8 to 35 μm and 1 to 20 μm, for Na3Co7(PO4)6-ST and Na3Co7(PO4)6-SG, respectively. Energy-dispersive X-ray Spectroscopy (EDS) confirms the presence of Na, Co, P, O elements and their homogenous distribution in the samples. The X-ray photoelectron spectroscopy (XPS) results indicate that the oxidation states for these elements are Na(I), Co(II/III), P(V) and O(-II). The optical bandgaps of Na3Co7(PO4)6-ST and Na3Co7(PO4)6-SG were estimated to be 1.79 eV and 1.78 eV, respectively, based on the UV–Vis diffuse reflectance spectra. The ionic conductivity for both samples is found to be 3.7 × 10-4 S/cm at 300 oC and 6.53 × 10-2 S/cm at 450 oC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.