Synthesis of multi‐block copolymer and its compatibilization to the blends of poly(ether ether ketone) with thermotropic liquid crystalline polymer

Abstract

AbstractA multiblock copolymer (BCP) containing amorphous poly(aryl ether ketone) (PAEK) and thermotropic liquid crystalline polymer (TLCP) segments was synthesized. The chemical structure and properties of BCP were characterized by fourier‐transform infrared spectrometer (FTIR), differential scanning calorimeter (DSC), gel permeation chromatograms (GPC), thermogravimetry analysis, polar light microscope (PLM), and solubility test respectively. BCP can dissolve in chloroform because of soluble PAEK block bonded with TLCP block, which was insoluble. The peak of the original PAEK oligomer was no more present in the GPC traces of the block copolymer. These facts indicated that polymer synthesized should be copolymers of the two components rather than blends. A single Tg at 138.1°C and broad melting endotherm at 315.7°C can be observed. The liquid crystalline texture of BCP showed uniformity in the view after heat treated for 10 min above its Tm under PLM. Ternary blends of poly(ether ether ketone) (PEEK)/TLCP/BCP were prepared by extrusion and characterized by DSC. DSC results showed that the crystallization temperature of PEEK phase in the blends shifted higher with the addition of TLCP. Wide angle X‐ray diffraction investigations indicated that the crystalline structure of PEEK was not disturbed by blending or compatibilizing. Scanning electron microscope and mechanical tests confirmed the compatibilizing effect of BCP. Reduction in dispersed phase TLCP size was observed when 2 phr by weight of compatibilizer was added to the blend. Measurement of the tensile properties showed increased elongation as well as improved modulus and strength to some extent. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2007