Synthesis of MnFe2O4 Spinel on Rusted Q235 Steel Surface and Its Corrosion Resistance Properties.

Abstract

Corrosion of steel is an issue that cannot be ignored in contemporary society. Due to large-scale corrosion, it is urgent to develop a surface treatment process that enhances the corrosion resistance of steel, allowing for application in various scenarios as needed. This study aims to investigate a novel surface treatment process to extend the service life of corroded Q235 steel, reduce its sensitivity to corrosion, and enable its use in multiple environments. This study employs the sol-gel method, using manganese nitrate solutions of varying concentrations to treat the surface of Q235 steel after different electrolysis times. The optimal conditions for precursor preparation were found to be a Mn2+ concentration of 0.1 mol/L and an electrolysis time of 2 h. Electrochemical tests using NaCl solutions of different concentrations revealed a significant reduction in the corrosion current for the composite coating based on Q235 steel treated with this method in NaCl solutions with wt.% = 1, 2, 3, 4, 5. Furthermore, the resistance to corrosion was strongest in the NaCl solution with a concentration of 1 wt.% where the corrosion current decreased from 24.8 µA/cm2 to 6.79 µA/cm2. Additionally, the coating was found to be diffusion-controlled in the early stages of the corrosion process and charge transfer-controlled in the later stages. The MnFe2O4 spinel coating demonstrated the greatest enhancement in corrosion resistance in the wt.% = 1 NaCl solution.