Abstract
Modulated elemental reactants were used to form amorphous ternary reaction intermediates of the desired compositions. The amorphous reaction intermediate for each system crystallizes exothermically below 200 °C forming kinetically stable “filled” skutterudites of general formula M1-xFe4Sb12 where M = Sn, Al, Ga, In, and Zn. These metastable compounds can only be prepared by controlling the reaction intermediates, avoiding the formation of more thermodynamically stable binary compounds. We propose that the desired compounds nucleate from the amorphous precursor because slow solid-state diffusion rates hinder disproportionation into the more stable mix of binary compounds and elements. If modulated elemental reactants are prepared with layer thicknesses above a critical value (∼40 A), the thermodynamically stable binary compound FeSb2 interfacially nucleates, preventing formation of the desired metastable ternary compounds. The use of low-angle X-ray diffraction and calorimetry provide the data necessary to...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.