Abstract
In this work, granule Li4Ti5O12 was successfully synthesized by spray drying a precursor slurry, followed by the solid-state reaction method. The precursor slurry was prepared from a solution of lithium carbonate (Li2CO3) and titanium dioxide (TiO2) in deionized water. A hybrid capacitor was fabricated which comprised a granule Li4Ti5O12 anode and activated carbon cathode. For comparison, an electrical double-layer capacitor (EDLC) cell was fabricated by using activated carbon electrodes in the same way. The electrochemical performance of the hybrid capacitor and the EDLC was characterized by constant current charge/discharge curves and cycle performance testing. The electrochemical testing results showed that the capacitance of the hybrid capacitor is approximately 2.5 times higher than that of the EDLC. Furthermore, the capacitance of the EDLC and the hybrid capacitor barely decreased after 1,000 cycles. The results of this study demonstrate that the hybrid capacitor has the advantages of the high rate capability of a supercapacitor (EDLC) and high battery capacity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.