Abstract
Infrared (IR) transparent Y2O3–MgO nanocomposites with a volume ratio of 50:50 were synthesized by combining colloidal and spark-plasma-sintering (SPS) techniques. In order to attain well-dispersed and homogeneous starting Y2O3–MgO nanopowder mixture, the effects of the pH value and the amount of polyetherimide (PEI) dispersant on the suspension stability were studied. Rheological measurement reveals that highly-dispersed and stable suspension was obtained at 7 wt% of PEI dispersant under pH = 10.6. The obtained nanopowders with particle size of 20–30 nm were densified using SPS at several sintering temperatures. The sintered composites show fine grains, narrow grain size distribution and uniform microstructure. The nanocomposite sintered at 1250 °C showed the maximum IR transmittance of 84% at a wavelength range of 2.5–6 μm. The Vickers hardness of the nanocomposite was about 11.9 ± 0.3 GPa, which is significantly higher than those of single phase MgO or Y2O3. Successful fabrication of the high-performance Y2O3–MgO nanocomposite indicates that i) the colloidal technique is an effect method to obtain highly dispersed and homogeneous nanopowders and ii) the SPS technique is a powerful tool to fabricate fine-grained dense transparent ceramics, which are suitable for fabricating IR transparent Y2O3–MgO composite ceramics from commercial starting powders.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.