Synthesis of high‐impact biodegradable multiblock copolymers comprising of poly(butylene succinate) and poly(1,2‐propylene succinate) with hexamethylene diisocyanate as chain extender

Abstract

AbstractBlock copolymers demonstrate excellent thermal and mechanical properties superior to their corresponding random copolymers and homopolymers. However, it is difficult to synthesize block copolymers comprising of different polyester segments by copolycondensation due to the serious transesterification reaction. In this study, multiblock copolymers comprising of two different polyester segments, i.e. crystallizable poly(butylene succinate) (PBS) and amorphous poly(1,2‐propylene succinate) (PPSu), were synthesized by chain‐extension with hexamethylene diisocyanate (HDI). Amorphous PPSu segment was incorporated to improve the impact strength of PBS. The copolymers were characterized by GPC, laser light scattering (LLS), NMR, DSC, and mechanical testing. The results of 13C NMR spectra suggest that multiblock copolymers with regular sequential structure have been successfully synthesized. The data of DSC and mechanical testing indicate that block copolymers possess excellent thermal and mechanical properties with satisfactory tensile strength and extraordinary impact strength achieving upto 1900% of pure PBS. The influence of PPSu ratio and chain length of both the segments on the thermal and mechanical properties was investigated. The incorporation of an amorphous soft segment PPSu imparts high‐impact resistance to the copolymers without obviously decreasing the melting point (Tm). The favorable mechanical and thermal properties of the copolymers also depend on their regular sequential structure. At the same time, the introduction of amorphous PPSu segment enhances the enzymatic degradation rate of the multiblock copolymers. Copyright © 2009 John Wiley & Sons, Ltd.