Abstract
Laser deposition was adopted to prepare novel Ni-based solid solution (γ-NiCrAlTi)/ TiC/α-Ti/CaF2 high-temperature self-lubricating wear resistant composite coating on Ti6Al4V alloy. Microstructure, micro-hardness, wear behavior, and counter-body effect of the coating were investigated systematically. It can be seen that the coating mainly consists of γ-NiCrAlTi, TiC, α-Ti, and small fine CaF2 particles. Average micro-hardness of the coating is 1023 HV0.3, which is about three-factor higher than that of Ti6Al4V substrate (380 HV0.3). The friction coefficient and wear rate of the coating decrease at all test temperatures to different extents with respect to the substrate. The improvement in wear resistance is believed to be the combined effects of the γ-NiCrAlTi solid solution, the dominating anti-wear capabilities of the reinforced TiC carbides, and the self-lubricating property of CaF2.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call