Abstract
Titanium aluminum carbide (Ti3AlC2 and Ti2AlC) powders were synthesized from TiH2 powders instead of Ti powders as Ti source by a tube furnace under argon atmosphere without preliminary dehydrogenation. 95 wt% pure Ti3AlC2 powders were synthesized from TiH2/1.1Al/2TiC at 1 450 °C for 120 min. High-purity Ti2AlC powders were also prepared from 3TiH2/1.5Al/C and 2TiH2/1.5Al/TiC powders at 1 400 °C for 120 min. The as-synthesized samples were porous and easy to be ground into powders. Sn or Si additives in starting materials increased the purity of synthesized Ti3AlC2 obviously and expanded the temperature range for the synthesis of Ti3AlC2. With Si or Sn as additives, high pure Ti3AlC2 was synthesized at 1 200 °C for 60 min from TiH2/x Si/Al/2TiC and TiH2/x Sn/Al/2TiC (x = 0.1, 0.2), respectively.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.