Synthesis of guanidinium‐based anion exchange membranes and their stability assessment

Abstract

Alkaline fuel cells potentially offer improved conversion efficiency and the prospect of using non‐noble metal catalysts; however, low conductivity and fast degradation of anion exchange membranes (AEMs) prevent their widespread application. In this work, a series of novel composite AEMs were synthesized by incorporating guanidinium‐based polymers into a porous polytetrafluoroethylene (PTFE) film. The guanidinium‐based polymers were polymerized using a condensation process between a guanidinium salt and two different diamines so that the guanidinium cations were tethered to the polymer backbone to enhance both conductivity and durability. In addition, polymer crosslinking was conducted to further reinforce the mechanical strength of the membranes and interlock the guanidinium moieties to the porous PTFE. It was found that the ionic conductivity of the synthesized membrane reached up to approximately 80 mS cm−1 at 20°C in deionized water. These membranes also exhibited superior stability compared to commercial quaternary ammonium AEMs after being exposed in 5 M KOH solution at 55°C for 50 h. Copyright © 2013 John Wiley & Sons, Ltd.