Abstract
Tilia wood was transformed by pyrolysis into carbon preform. This porous carbon preform was infiltrated with TEOS (Si(OC2H5)4), as a source of silica. In situ reaction between the silica and the carbon template occurred in the cellular wall at a hight temperature. Depending on the applied atmosphere, non-oxide (SiC) or oxide (SiO2) ceramics were obtained. Scanning electron microscopy (SEM), X-ray diffraction (XRD), infrared (IR) spectroscopy, mercury porosimetry and BET measurements were employed to characterize the phases and crystal structure of biomorphic ceramics. The experimental results showed that the biomorphic cellular morphology of the wood maintained in both the SiC and SiO2 ceramics, wich consisted of ?-SiC with trace of ?-SiC and SiO2, respectively. .
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.