Abstract
AbstractFor the sake of enhance the sinter ability and electrical conductivity of BaZr0.1Ce0.7Y0.2O3‐δ (BZCY) electrolytes, a modified aqueous gel‐casting method was applied to synthesize high sintering active and high conductive BZCY nano‐powders. The new approach makes it easy to obtain pure perovskite. The highly sintering active purity‐phase of BZCY nano‐powder (particle size of 50∼100 nm) was obtained by calcining at 1100°C for 2 h. Nano‐powders effectively reduce the sintering densification temperature and successfully prepare BZCY electrolyte with relative density > 96 % at 1450°C, and promote grain growth with an average grain size of 2.36 μm. Benefiting from this, improved electrical conductivities (e.g., 12.4×10−3 S cm−1 at 700°C, in wet air) are obtained. The NiO‐BZCY/BZCY/LSCF‐BZCY anode‐supporting single cell shows a peak power density of 0.75 W cm−2 at 700°C while taking ambient air as oxidants and wet H2 (∼3 vol.% H2O) as fuels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.