Abstract
In this study, Au:TiO2 nanoparticles (NPs) are prepared by using the laser ablation method in liquid at different laser energies (600, 800, and1000 mJ). After that, Au: TiO2 NPs were deposited on porous-Si(PS). Porous silicon (PS) is synthesized by using the photo-electrochemical etching (PECE) of n-type crystalline Si (c-Si) wafers of (100) orientation. The intensity of the etching current density was (4, 12, and 20 mA/cm2), with 16% (HF), and the etching time was 15 minutes. The X-ray diffraction (XRD) techniques, scanning electron microscopy (SEM), UV–visible spectrophotometry, and electrical properties are used to characterize the obtained particles. From the photo-detector measurements, the spectral responsivity curves three inclusive regions; the first peak was due to the absorption of UV light by Au: TiO2 NPs. The second peak was corresponding to the visible light absorption with the PS layer and the third peak was due to the absorption edge of the Si substrate. The higher responsivity of Au: TiO2 NPs/PS photo-detector was found to be 2.56A/W for specimens prepared at laser energy 800mJ.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.