Synthesis of activated carbon from oil fly ash for removal of H2S from gas stream

Abstract

Activated carbon (AC) is made from waste oil fly ash (OFA) which is produced in large quantities from power generation plants through combustion of heavy fuel oil. OFA contains ∼80% carbon that makes it suitable for producing AC by physicochemical treatments using a mixture of HNO3, H2SO4, and H3PO4 acids to remove non-carbonaceous impurities. The acid treated OFA is then activated by CO2 at 990°C. The physico-chemical treatments of OFA have increased the surface area from 4 to 375m2/g. Surface morphology and pore volume of AC are characterized by combined SEM and EDX techniques. Elemental analysis shows that sulfur content is reduced from 7.1wt% in untreated OFA to 0.51wt% for the treated OFA. The AC is further treated with HNO3 and NH4OH solutions in order to attach the carboxylic and amine groups on the surface, respectively. FTIR characterization is used to confirm the presence of the functional groups on the surface of AC at different stages of its development. The performance of functionalized AC samples is tested for the removal of H2S from a synthetic natural gas by carrying out breakthrough experiments. The results from these tests have shown maximum adsorption capacity of 0.3001mg/g for NH4OH functionalized activated carbon with 86.43% regeneration efficiency. The ammonium hydroxide treated AC is found to be more effective for H2S removal than acid treated AC as confirmed by breakthrough experiments. The results indicate that the presence of more acidic functionalities on the surface reduces the H2S adsorption efficiency from the gas mixture.