Abstract
A novel UV absorbent,(3-hydroxy-4-benzoyl)phenyl 2,3;4,6-di-O-cyclohexylidene-D-β-mannopyranoside(UV-O-DHM),was synthesized using 2,4-dihydroxy-benzophenone(UV-O) and D-mannose as raw materials.The compound exhibited high decomposition temperature(Td) at 372.6 ℃ and possessed good thermal stability.The biodegradable anti-UV polylactic acid(PLA) superfine fibrous membranes were prepared via electro-spinning through mixing UV-O-DHM into dichloromethane solution of PLA,and the features of the fiber were clearly characterized by scanning electron microscope.The fiber has uniform diameter of 3~4 μm and is evenly covered by the nano-porous.The UV-O-DHM/PLA superfine fiber has good ultraviolet absorption performance.With increasing concentration of UV-O-DHM,UV transmittance(T%) decreased,and when the mass fraction of UV-O-DHM was 1.1%,T% was almost 0 in 230~350 nm,and the UV protection level was better than that of UV-O/PLA superfine fiber in 365~380 nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.