Synthesis, characterization and thermoluminescence properties of MgB4O7 phosphor co-doped with Tm and Dy

Abstract

The luminescent and dosimetric properties of the MgB4O7 phosphor co-doped with Tm and Dy ions (MgB4O7:Tm,Dy) obtained by the solution combustion technique were investigated. With the prepared material, sintered dosimeters in pellet form were made. The MgB4O7 dosimeters doped with Tm and Dy with 0.25 and 0.10 mol% respectively and sintered at 1223 K for 3 h showed a sensitivity almost 11 times greater than the sensitivity of the TLD-100 commercial dosimeter. The TL response as a function of the gamma dose showed linearity up to 50 Gy followed by a supralinearity region and, above 500 Gy, the saturation region of the electron traps is reached. The fading of the main TL peak was negligible in the first five days after irradiation reaching 13% after 60 days and the lower detection limit was 43 μGy. The kinetic parameters were determined using the deconvolution method revealing general and second order kinetics. The morphology, crystallography and photoluminescence of the prepared phosphor samples are also reported.