Abstract
Pristine ZnO, Cu2+:ZnO, Ce3+:ZnO and Cu2+, Ce3+:ZnO nanopowders with different doping concentrations (0, 0.31, 0.62, 0.93 and 1.24% of dopant) were synthesized by sol–gel technique with low sintering temperature of 600 °C. The powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected-area electron diffraction (SAED), UV–Vis optical absorption and photoluminescence (PL) spectroscopy analysis. XRD patterns revealed that all the compounds are hexagonal wurtzite crystalline structure and that all the dopant atoms substituted Zn atoms in the ZnO lattice and there was no formation of extra Phases. SEM photographs displayed morphology of the prepared nanopowders. The UV–Vis absorption spectrum presented an absorption peak at 355 nm which was ascribed to ZnO nanoparticles. The photoluminescence spectrum displayed emission peaks at 486 nm and 527 nm. The 486 nm peak conformed to bandgap excitonic emission and the 527 nm peak was attributed to the existence of independently ionized oxygen vacancies. Sol–gel technique has capability for application in manufacturing units, because its process is simple and the reagents used are economical. Particle sizes in the range 10–51 nm were realized from the TEM analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.