Abstract
Photoluminescent properties of Sm3+/ Dy3+ single and co-doped SrZrO3 perovskites, prepared through conventional solid state ceramic route method were investigated. X-ray diffraction studies confirmed the orthorhombic (Pnma) perovskite structure of the calcined samples. Dy3+doped SrZrO3 systems showed blue emission at 482 nm and yellow emission at 574 nm due to the transition between 4F9/2-6H15/2 and 4F9/2-6H13/2 levels respectively while Sm3+ doped SrZrO3 systems shows red emissions at around 567 nm, 603 and 646 nm that respectively corresponds to the 4G5/2 → 6H5/2, 4G5/2 → 6H7/2 and 4G5/2 → 6H9/2 transitions of Sm3+. Sm3+/ Dy3+ co-doped SrZrO3 systems shows two different emissions for excitations at 350 nm and 407 nm. Near white light emission was achieved for the SrZr0.9Sm0.025Dy0.075O3, SrZr0.9Sm0.05Dy0.05O3 andSrZr0.9Sm0.075Dy0.025O3 systems at 354 nm excitation with CIE colour co-ordinates (0.3792, 0.3849), (0.3813, 0.3853) and (0.3786, 0.3851) respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.