Synthesis, characterization and evaluation of a fluorinated resin monomer with low water sorption

Abstract

A fluorinated acrylate monomer (4-TF-PQEA) without BPA (bisphenol-A) structure was synthesized and mixed with triethylene glycol dimethacrylate (TEGDMA) to used as dental resin system in order to achieve lower water sorption and reduce human exposure to BPA derivatives. Double bond conversion (DC) was measured using Fourier transform infrared spectroscopy (FTIR). Water sorption (WS), water solution (WL) and depth of cure (DOC) were evaluated according to ISO 4049:2009. Water contact angle (CA) was measured using contact angle analyzer. Polymerization shrinkage (PS) was evaluated according to the Archimedes' principle and ISO 17304:2013. Flexural strength (FS) and flexural modulus (FM) were measured by three-point bending test with a universal testing machine according to ISO 4049:2009. Comprehensive strength (CS) and vickers microhardness (VM) were also investigated. Thermal stability test was measure by Thermogravimetric analyzer. Cytotoxicity of three resin systems was tested through MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazoliumbromid) cytotoxicity method according to the ISO 10993-5:2009. Bisphenol-A glycidyl dimethacrylate (Bis-GMA)/ TEGDMA resin system was used as a control. The results show that 4-TF-PQEA/TEGDMA resin system had lower PS, lower WS and higher DC values than those of Bis-GMA/TEGDMA resin system except some mechanical properties, such as FS, FM and CS. Moreover, properties of other 4-TF-PQEA-containing resin systems were also comparable with those of Bis-GMA/TEGDMA resin system. In particular, the overall performance of resin system consisted of 4-TF-PQEA/Bis-GMA/TEGDMA is optimized when the mixture ratio is 30/40/30(wt/wt/wt). Therefore, the 4-TF-PQEA has potential to be used as resin monomer for dental resin composites to achieve lower water sorption.