Polysaccharide-structured copolymer hydrogel having excellent pH-sensitivity was developed from N,N-dimethylacrylamide (DMAc) and vinyl-functionalized Pectin (Pec). The Pec was vinyl-functionalized by way of chemical reaction with glycidyl metacrylate (GMA) in water under acidic and thermal stimuli. 13C NMR, 1H NMR, and FT-IR spectra revealed that the vinyl groups coming from the GMA were attached onto backbone of the polysaccharide. The hydrogels were obtained by polymerization of the Pec-vinyl with the DMAc. 13C-CP/MAS NMR and FTIR spectra confirmed that the gelling process occurred by way of the vinyl groups attached on Pec-vinyl backbone. The values of apparent swelling rate constant (k) decreased appreciably for pH greater than 6, demonstrating the swelling process of the hydrogel becomes slower at more alkaline conditions. There was an increase of diffusional exponent (n) with increasing pH of the surrounding liquid. This means the water absorption profile becomes more dependent on the polymer relaxation in basified swelling media. In this condition, a longer water absorption half-time (t1/2) was verified, suggesting the polymer relaxation mechanism of the hydrogel would have a considerable effect on the t1/2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.