Synthesis and thermal degradation mechanism of polyorganocarboranesiloxanes containing m-carboranylmethyl unit

Abstract

This paper reports a high-yielding, efficient and facile method in preparing monomers, namely 1,7-bis(hydroxyl(dimethyl)silylmethyl)-m-carborane (M1), 1,7-bis(diethylamino(dimethyl)silylmethyl)-m-carborane (M2), 1,3-dimethyl-1,3-diphenyl-siloxanediol (M3) and diethylaminomethylphenylsilane (M4). The reaction of M2 and M3 to get polymer P1, and the reaction of M1 and M4 to get polymer P2 which has a promising lead in searching for materials with high-temperature properties. The structure of monomers and linear polymers were characterized by NMR and FTIR. Thermal properties of the polyorganocarboranesiloxane elastomers were characterized by DSC and TGA. The results showed that elastomers E1 and E2 have better thermal stability and thermal oxidative stability with 5% weight loss temperatures above 570 °C, 650 °C in nitrogen and 536 °C, 730 °C in air, respectively than that of linear polymers P1 and P2. The highlight was to study the thermal degradation mechanism of polyorganocarboranesiloxane elastomers using XPS and Solid-state 29Si NMR. Carborane and organosiloxane outside of samples were gradually oxidized to B2O3 and SiO2 respectively, the inside only occurred the cleavage of the Si-Ph bond caused by terminal hydroxyl groups which resulted in chain branching and illustrated there was no access for oxygen easy to internal oxidation.