Abstract
We report synthesis and superconductivity at 3.7 K in PrO0.5F0.5BiS2. The newly discovered material belongs to the layered sulfide based REO0.5F0.5BiS2 compounds having a ZrCuSiAs-type structure. The bulk polycrystalline compound is synthesized by the vacuum encapsulation technique at 780 ∘C in a single step. Detailed structural analysis has shown that the as synthesized PrO0.5F0.5BiS2 is crystallized in a tetragonal P4/nmm space group with lattice parameters a=4.015(5) Å, c=13.362(4) Å. Bulk superconductivity is observed in PrO0.5F0.5BiS2 below 4 K from magnetic and transport measurements. Electrical transport measurements showed superconducting transition temperature (T c ) onset at 3.7 K and T c (ρ=0) at 3.1 K. The hump at T c related to the superconducting transition is not observed in the heat capacity measurement and rather a Schottky-type anomaly is observed at below ∼6 K. The compound is slightly semiconducting in a normal state. Isothermal magnetization (MH) exhibited typical type II behavior with a lower critical field (H c1) of around 8 Oe.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.