Abstract
Nano crystalline spinel ferrites of Co0.5Ni0.5CexFe2−xO4 (x=0.01, 0.015, 0.02, 0.025 and 0.03) was prepared by modified solution combustion method using a mixture of fuels for the first time. The influence of rare earth Ce3+ substitution at the Fe3+ site on the structural, microstructural and dielectric properties of Co0.5Ni0.5CexFe2-xO4 was investigated. The X-ray diffraction (XRD) studies confirmed the formation of monophasic nano crystalline samples without any secondary phases. The crystallite size decreases and density increases with the increases of Ce3+ contents. Surface morphology was studied through Scanning Electron Microscopy (SEM). Dielectric properties of these ferrites have been studied at room temperature using impedance analyzer in the frequency range up to 20 MHz. The effect of frequency and composition on dielectric constant (e’), dielectric loss (tanδ) and ac conductivity (σac) have been discussed in terms of hopping of charge carriers (Fe2+↔Fe3+). The decrease in dielectric loss with frequency follows Debye’s relaxation phenomena. Both the variation in tan loss and dielectric loss with frequency shows a similar. AC conductivity increases with the increases of frequency which directly proportional to concentration of Ce3+ ions follows Jonscher law. These Cerium doped Cobalt-nickel ferrites are very helpful for automotive applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.