Abstract
Two microsamples of 244Cm-Co alloys prepared by high-temperature condensation of curium metal vapor onto flat cobalt supports were studied. Both samples contained two intermetallic compounds with hexagonal lattices: Co17Cm2 and Co5Cm. The existence of Co2Cm or Co2(Cm,Th) intermetallic compound with a cubic lattice was assumed. It was found that Cm is insoluble in α- and β-Co at room temperature and at heating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.