Synthesis and Structure of Lithium Cadmium Selenite Hydroxide, LiCd2(SeO3)2(OH)

Abstract

The new compound LiCd2(SeO3)2(OH) has been hydrothermally synthesized and characterized by single-crystal X-ray diffraction and IR spectroscopy. It is built up from a network of edge- and vertex-sharing pyramidal [SeO3]2— groups, distorted CdO6 octahedra, and CdO7 monocapped trigonal prisms. The cadmium-centred groups form infinite columns, onto which Se atoms (as [SeO3]2— groups) are grafted. Cross-linking between the columns results in a three-dimensional framework which encapsulates [100] channels occupied by the tetrahedrally-coordinated lithium cations. The H atom of the hydroxyl group appears to participate in a weak, bifurcated, hydrogen bond. Crystal data: LiCd2(SeO3)2(OH), Mr = 502.67, monoclinic, P21/c (No. 14), a = 5.8184 (3)A, b = 10.2790 (5)A, c = 11.5021 (5)A, β = 90.446(1)°, V = 687.89 (9)A3, Z = 4, R(F) = 0.021, wR(F2) = 0.046. Synthese und Struktur von LiCd2(SeO3)2(OH) LiCd2(SeO3)2(OH) wurde hydrothermal dargestellt und durch Einkristall-Rontgenbeugung und IR-Spektroskopie charakterisiert. Die Verbindung wird von einem Gitter aus kanten- und eckenverbruckten pyramidalen [SeO3]2—-Gruppen, verzerrten CdO6-Oktaedern und einfach-bekappten trigonalen CdO7-Prismen aufgebaut. Die CdO6- und CdO7-Polyeder bilden unendliche Kolonnen, in denen Se-Atome (als [SeO3]2—-Gruppen) verbunden sind. Vernetzung zwischen den Kolonnen ergibt ein dreidimensionales Gitter, das [100]- Kanale einschliest, die von tetraedrisch-koordinierten Lithium-Kationen besetzt werden. Die Wasserstoffatome der Hydroxyl-Gruppen scheinen an einer schwachen, gegabelten Wasserstoffbruckenbindung beteiligt zu sein. Kristalldaten s. Abstract.