Abstract
Abstract The series of La1-xPrxGa0.5Sb1.5O6 solid solutions (x = 0–1) with PbSb2O6 structure was synthesized. The comparative study of the La1-xPrxGa0.5Sb1.5O6 morphology showed all compounds have net microstructures. Herein the Pr concentration increasing leads to particles size decreasing from 400 up to 200 nm in the samples with low Pr content and to recrystallization and coarsening of the particles in Pr-rich ones. Using LaGa0.5Sb1.5O6 as an example, it was shown that the compounds have a wide transmission region in the visible and IR spectral ranges and are characterized by a low-energy phonon spectrum. An analysis of the spectral-luminescent characteristics revealed the presence of a cross-relaxation process (1D2→1G4) → (3H4→3F4) of Pr3+ ions for La1-xPrxGa0.5Sb1.5O6 at x ≥ 0.07. It was showed that a broadband radiation of thermal nature is observed under laser excitation with λ = 457 nm and a power density of J = 4.65 kW/cm2 for the samples with high (x = 0.4–1) praseodymium content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.